Products - Fire Clay High Alumina Bricks
 

FIRE CLAY & HIGH ALUMINA BRICKS

Brand Name

Al2O3
(%)
Min

Fe2O3
(%)
Max

A.P. (%)
Max

B.D.
(gm/cc)
Min

CCS
(kg/cm2)
Min

PLC
(%)
Max.

PCE
(SK)
Min

RUL
Ta(0C)
Min

Application Area

MPR –BF

36

1.70

18

2.15

300

± 0.30
at 1450 0C/ 2 hrs

31

1450

Blast Furnace Stack Lining

MPR –BF-D

42

1.50

16

2.25

400

± 0.5
at 1450 0C/ 2 hrs

33

1500

Blast Furnace Lining

MPR-45 N

45

1.50

21

2.20

350

± 0.50
at 1500 0C/ 2 hrs

34

1450

Blast Furnace lining, cement rotary kiln lime calcinations kiln, glass tank furnace

MPR-45 D

45

1.50

16

2.30

450

± 0.30
at 1450 0C/ 2 hrs

34

1500

-do-

MPR 50 D

50

1.30

18

2.35

350

± 0.30
at 1500 0C/ 2 hrs

34

1530

Anode baking furnace

MPR -55D

55

1.50

18

2.40

500

± 0.50
at 1450 0C/ 2 hrs

35

1520

Blast Furnace lining, cement rotary kiln, lime calcinations kiln, glass tank furnace

MPR-LF -60

59

1.20

18

2.50

500

± 0.50
at 1450 0C/ 2 hrs

36

1600

BF hot blast main, glass tank furnace.

MPR-LF -50

50

1.10

18

2.40

400

± 0.5
at 1450 0C/ 4 hrs

34

1520

Anode baking furnace

MPR –SIC -AL-65

65

1.50

12

2.65

400

-

36

1650

Torpedo Ladle

MPR 45 B

45

3.5

22

2.25

300

± 1.5
at 1350 0C/ 2 hrs

33

1350

Cement Plants

MPR 50 B

50

3.5

22

2.30

350

± 1.5
at 1400 0C/ 2 hrs

33

1370

-do-

MPR-60B LF

60

2.50

22

2.45

450

± 2.0
at 1450 0C/ 2 hrs

35

1420

 

MPR -60 B

60

3.00

22

2.40

400

-do-

34

1400

 

MPR  - 62

62

1.50

22

2.40

350

± 0.40
at 15000C/ 2 hrs

36

1500

Blast furnace stove checkers, BF lining

 

FIRE CLAY & HIGH ALUMINA BRICKS

Brand Name

Al2O3
(%)
Min

Fe2O3
(%)
Max

A.P. (%)
Max

B.D.
(gm/cc)
Min

CCS
(kg/cm2)
Min

PLC
(%)
Max.

PCE
(SK)
Min

RUL
Ta(0C)
Min

Application Area

MPR  -62 D

62

1.20

16

2.50

600

± 0.20
at 15000C/ 2 hrs

36

1550

Blast furnace hearth & tuyere

MPR 62 LF

62

1.2

18

2.52

500

± 0.3
at 15000C/ 2 hrs

36

1600

Blast Furnace checkers

MPR-70  LF

70

1.5

20

2.60

500

± 0.3
at 15000C/ 2 hrs

36

1550

Rotary Kiln Lining

MPR-Mul -70  S

70

0.80

20

2.50

500

± 0.20
at 15000C/ 2 hrs

36

1700

Blast Furnace hearth & tap hole, glass tank furnace

MPR-Mul-70 (F)

70

0.5

17

2.55

600

± 0.20
at 15000C/ 2 hrs

36

1720

Blast Furnace hearth & tap hole, glass tank furnace

MPR-70 B (LF)

70

2.5

20

2.60

500

± 0.30
at 16000C/ 2 hrs

36

1480

EAF roof, ladle

MPR -70 B

70

3.0

22

2.55

450

± 0.30
at 16000C/ 2 hrs

35

1440

EAF roof

MPR-80B (LF)

80

2.5

20

2.70

500

± 0.30
at 16000C/ 2 hrs

37

1500

-do-

MPR -80 B

80

3.0

22

2.70

500

± 3.0
at 16000C/ 2 hrs

35

1460

-do-

MPR-85 TAB

84

1.5

20

2.70

700

± 0.5
at 15000C/ 2 hrs

37

1580

Aluminum melting & holding furnace.

MPR-85  D

85

1.5

20

2.90

500

±0.5
at 15000C/ 2 hrs

37

1650

Torpedo ladle lining

MPR 88 NF

88

2.0

18

2.85

800

± 0.5
at 15000C/ 2 hrs

37

1580

Reheating furnace hearth

MPR-90 LF

90

0.5

18

2.92

600

± 0.2
at 15000C/ 2 hrs

38

1700

Carbon black reactor

MPR-95

95

0.5

22

3.00

600

± 0.2
at 15000C/ 2 hrs

38

1700

Secondary Steel making Vessel, Chemical,
Petrochemical & Fertilizer application.

 